Blast furnace refractories:

Development of blast furnace ceramic cup increasingly common, but require high corrosion resistance of refractories application to ensure its life extended. In addition to changes in the design of the refractory material respects, great changes have taken place, such as a micro porous carbon brick ordinary charcoal instead of the past in order to reduce the penetration of molten iron. Clay refractory bricks used as raw material can adapt to the requirements stemming mouth of iron. Grouting method using blast furnace repair backing backing can effectively prevent the erosion of hot air, thereby extending the life of the blast furnace lining.

Clay refractory bricks used as raw material can adapt to the requirements stemming mouth of iron. Grouting method using blast furnace repair backing backing can effectively prevent the erosion of hot air, thereby extending the life of the blast furnace lining.
Converter refractories:
In steelmaking, the kind of water-cooled technolovgy and suspension systems are in the upper part and the lower cone barrel parts BOF shell has been applied, thus reducing the converter furnace deformation, extending converter lining life, improve productivity converter. These new technologies have some impact on the use of refractories. So that the converter furnace furnace up to 4000 more than the average, combined with gunning, the application of high lime and dolomite applications and slag splashing technology, furnace over 10,000 times is not a problem. This is the direction of development of refractories producer worth attention.
Submerged nozzle for continuous casting:
Since the development of the system of casting tundish transfer station from the past into the present effects of cast steel quality and increase the productivity
of the metallurgical vessel. Therefore, many functional materials gradually applied in the middle of the package, such as slag dam, impact plates, filters, plugs, etc. argon permeability.
Submerged nozzle as an important function of continuous casting refractories, research carried out mainly focused on two aspects, one is to improve the corrosion resistance of slag line, the second is to reduce the inner wall of Al2O3 attachment. Take the ZrO2 content increased 88%, as well as a good measure of the particle size distribution can reduce the thermal expansion coefficient and porosity of products, improve the density improvement slag resistance.