The Best Refractories for Induction Furnace — 25+ Heats Silica Ramming Mass

In recent years, silica ramming mass is widely used in induction furnace. Compared with traditional refractory lining material, this product is of lower cost, shorter sintering time and better working condition.

To offer clients better refractory products, we have successfully developed our 25+ heats silica ramming mass. As per actual working, we summed up the material consumption as following.

1. First heat: 10-15mm
2. Rest heat: 3-5mm

As per our experience, we should leave 70mm as save level. So if the

lining thickness is 180/300/450mm, we could promise the least service life of ourrefractory material to be 25 heats. If the working condition is convenient, 30-40 heats is no problem.

Furthermore, our silica ramming mass can also be applied in tundish and ladle. Service life can namely be 48-60 hours/ 200+ heats.

Because of the great advantages as above, our silica ramming mass is very welcomed by our clients all over the world say Bangladesh, Ghana, South Africa, and Indonesia, etc. If more interests, please feel free to make us informed, our professional teams are ready to give you our reliable service. For new clients, we would offer more preferential as following.

1. Lower price trial order
2. Professional refractory technicians overseas service

Therefore, what are you waiting for? Take your phone and contact us!

How to distinguish the quality of the refractory brick

In general, according to the contents of various chemical compositions and their functions, it is divided into three categories, which are the main components, impurities, and the added ingredients.

The main component of the refractory brick is the majority of the material, the high temperature properties of the chemical composition of the decisive role. Refractory brick why can have excellent resistance to high temperature, and many refractory materials and characteristics? Completely or basically according to the contents of various chemical components in the refractory materials and its role, usually the main components, impurities and the composition of the three types of.

Impurities are those in refractory material in different principal component, content of fractional and high heat resistance properties of the refractory often bring the harm of chemical composition. This chemical composition is mainly composed of the raw material in the entrainment and come.

The main component of the refractory brick is the majority of the material; the high temperature properties play a decisive role in chemical composition. Refractory brick has good resistance to high temperature performance, as well as many refractory materials and their own characteristics, completely or basically depends on the principal components. Therefore, the main ingredient of refractory materials must be fully paid attention to. Usually on refractory materials according to the chemical composition and classification, and on many of the same material refractory material is divided into several levels, is mostly according to the main components of the kinds and content of the amount. Can be used as refractory materials are main components with a high melting point high lattice energy or high temperature decomposition of elements or compounds.

The price of refractory brick should be determined by the type of refractory brick, which is based on the type of output and the type of refractory brick.